Título : Desempenho em fadiga e corrosão-fadiga da liga Ti-35Nb-2,5Sn laminada a quente aplicada como biomaterial
Otros títulos : Fatigue and corrosion-fatigue performance of the hot rolled Ti-35Nb-2,5Sn alloy applied as a biomaterial
Autor : Andrade, Carlos Eduardo Celestino de
Fecha de publicación : 27-sep-2013
Director(a): Griza, Sandro
Resumen: Os materiais metálicos biomédicos apresentam notável importância na reconstrução de tecidos estruturais que falharam. Atualmente, a produção de novas ligas de titânio tem sido incentivada para uso biomédico a fim de reduzir as limitações quanto ao módulo de elasticidade e citotoxicidade das ligas comercializadas, em particular a liga Ti-6Al-4V. As ligas de Ti-Nb-Sn surgem como alternativa para esta finalidade. No estudo atual, ligas de Ti-35Nb-2,5Sn foram obtidas por fusão a arco voltaico, solubilizadas, laminadas a quente com 40 % de redução e resfriadas em água. O teor de nitrogênio e oxigênio foi verificado por fusão em ambiente de gás inerte. As microestruturas foram caracterizadas por microscopia ótica, microscopia eletrônica de varredura (MEV) e difração de raios-X. Corpos de prova de fadiga foram usinados e submetidas a ensaio para obtenção de curvas S-N ao ar e em ambiente com 0,9 % de NaCl e baixa frequência. Os micromecanismos de fratura foram analisados em microscópio eletrônico de varredura (MEV). Os resultados foram comparados com os dados publicados na literatura para outras ligas beta estabilizadas e foram discutidos os potenciais de aplicação das novas ligas. Os resultados dos ensaios mostraram que o limite de fadiga tende a coincidir com a tensão limite para o início do movimento de discordâncias.
Resumen : Metallic materials have considerable importance in biomedical tissue reconstruction structural failed. Currently, the production of new alloys, titanium has been encouraged for biomedical use so as to reduce limitations and elastic modulus of alloy marketed cytotoxicity, in particular Ti-6Al-4V. Alloys Ti-Nb-Sn are an alternative for this purpose. In the current study, alloy Ti-35Nb-2,5SN were obtained by melting the arc, solubilized at 1000 ° C for 12 hours, hot-rolled with 40% reduction in water and cooled. The content of nitrogen and oxygen was verified by melting in an atmosphere of inert gas. The microstructures were characterized by optical microscopy, scanning electron microscopy (SEM) and X-ray diffraction. The characteristics in fatigue and corrosion - fatigue alloy were determined according to the guidelines noted in ASTM E466. Specimens were machined and fatigue SN curves obtained in air and in an environment with 0.9% NaCl. The micromechanics of fracture were analyzed by scanning electron microscope (SEM). The results were compared with published data for beta stabilized alloys and discussed the potential application of new alloys.
Palabras clave : Materiais
Ligas de titânio
Materiais - Fadiga
Metais - Fadiga
Materiais - Deterioração
Metais - Corrosão
Ligas de titânio - Corrosão
Corrosão-fadiga
Tratamento termomecânico
Materials
Materials
Materials
Metals
Metals
Titanium alloys
Titanium alloys
Área CNPQ: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Idioma : por
Programa de Posgrado: Pós-Graduação em Ciência e Engenharia de Materiais
Tipo de acceso: Acesso Aberto
URI : https://ri.ufs.br/handle/riufs/3494
Aparece en las colecciones: Mestrado em Ciência e Engenharia de Materiais

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
CARLOS_EDUARDO_CELESTINO_ANDRADE.pdf2,98 MBAdobe PDFVista previa
Visualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.