Título : Caracterização e viabilidade do uso de hidrogéis compósitos poli (álcoolvinílico)/atapulgita em sistemas de liberação de fármaco
Otros títulos : Characterization and viability of poly (vinyl alcohol)/ attapulgite composites hydrogels in drug delivery system
Autor : Santana, Genelane Cruz
Fecha de publicación : 10-feb-2012
Director(a): Barreto, Ledjane Silva
Resumen: Foram desenvolvidos hidrogéis compósito na forma de filme a base de poli (álcool vinílico) (PVA) usando a atapulgita acidificada como agente de reticulação. Os hidrogéis compósitos foram obtidos em solução variando a quantidade de atapulgita (0,05-2%) na matriz polimérica visando estudar sua influência na cristalinidade, nas propriedades de intumescimento e na liberação do sulfato de gentamicina. Os materiais preparados foram caracterizados por DRX, FTIR, DSC. Segundo os dados do DRX a cristalinidade do polímero não é afetada pela adição da argila, em contrapartida, a presença da atapulgita altera as temperaturas de fusão e cristalização, comportamento verificado pelo DSC. De maneira geral, o perfil gráfico do FTIR evidenciou que há interações entre a atapulgita e o PVA. A cinética de hidratação a 37°C mostrou ser independente do valor de pH e demostrou obedecer ao mecanismo de difusão fickiana com valores de n<0,5. Desse modo, a viabilidade dos hidrogéis em sistema de liberação de fármacos foi avaliada pelo grau de intumescimento e liberação in vitro. Estes dois aspectos foram dependentes da concentração do fármaco. Assim, apesar de preliminares, os resultados de liberação do sulfato de gentamicina utilizando hidrogéis compósito PVA/ atapulgita mostraram-se promissores para uma futura aplicação.
Resumen : Composites hydrogels were developed in film shape based on poly vinyl alcohol (PVA) using acidified attapulgite as crosslinking agent. The hydrogel composites were obtained in solution with amounts of attapulgite ranging from 0.05 to 2% in the polymer matrix in order to study its influence on the crystallinity, in the swelling properties and in the release of gentamicin sulphate. The obtained composites were characterized by XRD, FTIR and DSC. According to XRD data the polymer crystallinity is not affected by the clay addition, however, the presence of attapulgite modifies the melting and crystallization temperatures, behavior observed by DSC measures. In general, graphical profile of FTIR showed that there are interactions between PVA and attapulgite. The hydration kinetics at 37°C is independent of pH values and shown to obey the Fickian diffusion mechanism with values of n<0.5. Thus, the viability of hydrogels in drug delivery systems was evaluated by the swelling degree and by in vitro release. These two aspects were dependent on the concentration of the drug. Thus, although preliminaries, the results from release of gentamicin sulphate using PVA/attapulgite composites hydrogels proved be promising for future application.
Palabras clave : Hidrogel
Atapulgita
Hidrogéis compósitos
Sistemas de liberação
Hydrogel
Attapulgite
Composites hydrogels
Delivery systems
Área CNPQ: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Patrocinio: Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
Idioma : por
PaÍs: BR
Institución / Editorial : Universidade Federal de Sergipe
Institución: UFS
Programa de Posgrado: Pós-Graduação em Ciência e Engenharia de Materiais
Tipo de acceso: Acesso Aberto
URI : https://ri.ufs.br/handle/riufs/3521
Aparece en las colecciones: Mestrado em Ciência e Engenharia de Materiais

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
GENELANE_CRUZ_SANTANA.pdf1,9 MBAdobe PDFVista previa
Visualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.