Síntese e caracterização estrutural e magnética das perovskitas complexas ReFe0:5M0:5O3 (Re = Dy, Gd, Sm, Eu,Nd ; M= Mn,Al)

Abstract

Samples of Bi 2Fe4O9 mullite and ReFe 0.5M0.5O3 (Re = Nd, Sm, Eu, Gd, Dy; M = Mn, Al) complex perovskites were successfully synthesized by using the combustion synthesis method. While the mullite was obtained after thermal treatment at temperatures below 1000ºC, complex perovskites are produced after thermal treatments between 1250ºC and 1500ºC for at most 24 h. The X-ray diffraction data analysis suggests the formation of single phase orthorhombic structure, after suitable heat treatment. Scanning electron microscopy (SEM) revealed the formation of micrometric grain size, giving to the sample the relative density. EDS spectra confirmed the homogeneity and purity of complex perovskites. Magnetization measurements as a function of field and temperature showed the diversity of magnetic behavior of the samples. Among the behaviors we can highlight the reorientation of spin for ortoferritas ReFe0.5Mn0.5O3 (Re = Dy, Gd, Eu, Sm, Eu) and ReFe0.5Al0.5O3 (Re = Dy, Nd). Another interesting finding was the effect of magnetic reversal of the samples ReFe0.5Al0.5O3 (Re = Nd, Gd) and EuFe0.5Mn0.5O3. Raman spectra show anomalous bands of second order in the perovskite DyFe0.5Al0.5O3 with characteristics of resonant effects. The evolution of the band associated with the symmetric vibrational mode of the octahedron shows hardening at the temperature range of ordered magnetic phase, thus suggesting a possible spin-phonon coupling. Depolarization current measurements highlights a relaxation process due to charge carriers in the samples ReFe0.5Mn0.5O3 (Re = Dy, Gd). The application of magnetic field profoundly influences the depolarization current behavior of DyFe0.5Mn0.5O3. Dielectric permittivity measurements showed no anomalies between 10 K and 300 K, that could can be associated to a ferroelectric phase.