Title: Estudo de comportamento mecânico de ligas TiNbSn em função do teor de liga, laminação a frio e envelhecimento
Other Titles: Study of mechanical behavior of TiNbSn alloy in the function of alloy content, cold lamination and aging
Authors: Azevedo, Thiago Figueiredo
Issue Date: 23-Aug-2017
Advisor: Griza, Sandro
Resumo : O presente estudo está focado em propriedades mecânicas resultantes de tratamentos de laminação a frio e envelhecimento aplicados a ligas de TiNbSn compreendendo diferentes conteúdos Nb (35% e 42%) e Sn (0% e 2,5%). As ligas foram fundidas a arco, homogeneizadas, solubilizadas, laminadas a frio e envelhecidas a 400°C durante diferentes tempos de envelhecimento. Um conjunto de ensaios de caracterizações, incluindo análise microestrutural, DRX, ensaios de tração, tenacidade (J) e análise de fraturas. As ligas apresentaram as mesmas fases beta, α" e ômega após laminação a frio, independentemente do teor de liga. O efeito da solução sólida levou a mudanças nas propriedades mecânicas. Além disso, as ligas apresentaram precipitação em fase alfa e conduziram a um estágio de pico após diferentes tempos de envelhecimento devido ao teor de Nb. As ligas contendo teor de Nb de 42% e 35% atingiram o ponto de pico de envelhecimento dentro de 48 e 72 horas, respectivamente. A precipitação da fase alfa nas ligas no ponto de pico aumentaram a dureza, a resistência à tração e o módulo de elasticidade das ligas. No entanto, também causou diminuição da ductilidade e da tenacidade. Os precipitados finos dispersos da fase alfa geraram microcavidades pequenos e pouco profundos, que são micromecanismos característicos de fratura de ligas de ponto máximo de envelhecimento.
Abstract: The present study is focused on mechanical properties that result from cold rolling and aging treatments applied to TiNbSn alloys comprising different Nb (35% and 42%) and Sn (0% and 2.5%) contents. The alloys were arc melted, homogenized, solubilized, cold rolled and aged at 400 °C for different aging times. A set of characterization tests performed, included microstructural analysis, X-ray diffraction, microhardness, tensile tests, toughness (J) and fracture analysis. The alloys contained all three beta, α” and omega phases after cold rolling, regardless of the alloying content. The solid solution effect led to changes in the alloys’ mechanical behavior. Furthermore, the alloys presented alpha phase precipitation, and it led to a peak-aged stage after different aging times due to the Nb content. The alloys containing 42% and 35% Nb content reached the peakaged stage within 48 and 72 h, respectively. The α phase precipitation in the alloys at peak-aged stage increased the hardness, tensile strength and elastic modulus of the alloys; however, it also caused ductility and toughness decrease. The fine dispersed precipitates of the alpha phase generated small and shallow dimples, which are a characteristic fracture micromechanism of peak-aged alloys.
Keywords: Materiais
Ligas de titânio
Metais -- Propriedades mecânicas
Mecânica da fratura
Ligas de titânio
Ligas TiNbSn
Propriedades mecânicas
Mecânica da fratura
Trabalho a frio
Deformação a frio
Envelhecimento
Mechanical properties
Fracture mechanics
Cold working
Aging
Subject CNPQ: ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Language: por
Country: Brasil
Publisher / Institution : Universidade Federal de Sergipe
Institution: UFS
Program Affiliation: Pós-Graduação em Ciência e Engenharia de Materiais
Citation: AZEVEDO, Thiago Figueiredo. Estudo de comportamento mecânico de ligas TiNbSn em função do teor de liga, laminação a frio e envelhecimento. 2017. 121 f. Tese (Doutorado em Ciência e Engenharia de Materiais) - Universidade Federal de Sergipe, São Cristóvão, SE, 2017.
Rights: Acesso Aberto
URI: https://ri.ufs.br/handle/riufs/3475
Appears in Collections:Doutorado em Ciência e Engenharia de Materiais

Files in This Item:
File Description SizeFormat 
THIAGO_FIGUEIREDO_AZEVEDO.pdf6,76 MBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.