Title: Compósitos à base de resina epóxi reforçados com fibra de coco
Other Titles: COMPOSITES BASED ON EPOXY RESIN REINFORCED WITH COCONUT FIBER
Authors: Gonçalves, Jorge Antônio Vieira
Issue Date: 25-Feb-2010
Advisor: Macêdo, Marcelo Andrade
Resumo : Compósitos poliméricos reforçados com fibras sintéticas são de grande interesse na indústria automobilística, merecendo destaque as resinas epoxídicas reforçadas por fibras de vidro. No entanto, estas fibras apresentam comportamento abrasivo causando desgastes dos equipamentos, tornando-se susceptíveis à perda de propriedades, devido à quebra das fibras durante o processamento, alto custo de fabricação. Por sua vez, o interesse de empresas e pesquisadores por compósitos alternativos, que utilizem recursos renováveis, apresentem baixo custo e sejam biodegradáveis, tem aumentado. A utilização de fibras vegetais em termorrígidos nas aplicações comerciais tem sido promissora, tendo em vista que elas não são tóxicas, possuem baixo custo, são de fontes renováveis e atendem as novas exigências de preservação ambiental. Além disso, as fibras vegetais não são abrasivas a equipamentos de processo e geram compósitos com baixa susceptibilidade a perda de propriedades durante o processamento. Entre a grande variedade de fibras vegetais existentes, a fibra de coco (subproduto do coco), abundante no Estado de Sergipe, com diâmetro médio de 0,25 milímetros e densidade inferior a das fibras de vidro, foi estudada como componente de reforço na matriz epóxi (DGEBA),nos teores de 0, 10, 20 e 30% em peso, contínua e orientada aleatoriamente. Estes compósitos foram ensaiados em tração e flexão e sua superfície analisada por microscopia eletrônica de varredura (MEV). Dentre as propriedades avaliadas, o aumento no teor de reforço provocou um acréscimo significativo da resistência à tração e flexão e do módulo de elasticidade dos compósitos comparados com a resina pura. As observações microestruturais revelaram os mecanismos de falhas que podem ocorrer durante a fratura; e que a superfície singular da fibra de coco contribui para uma boa adesão com a DGEBA (diglicidil éter do bisfenol A).
Abstract: Polymer composites reinforced with fibers are of great interest in the automotive industry, with emphasis to epoxy resin reinforced with glass fibers However, these fibers exhibit abrasive behavior causing wear of equipment, making it susceptible to the loss of properties due to the breakdown of fibers during processing, high cost of manufacturing. In turn, the interest of companies and researchers for composite alternatives, using renewable resources, having a low cost and being biodegradable, has increased. The use of vegetable fibers in thermosetting in commercial applications has been promising, considering that they are not toxic, have low cost, are renewable sources and meet the demands of environmental preservation. In addition, the vegetable fibers are not abrasive to processing equipment and create composites with low susceptibility to loss of properties during processing. Among the wide variety of existing plant fibers, coir (coconut product), abundant in the state of Sergipe, with an average diameter of 0.25 mm and lower density than the glass fibers, it was studied as a strengthening component in the epoxy matrix (DGEBA), at the levels of 0, 10, 20 and 30% by weight, continuous and randomly oriented. These composites were tested in tension and bending and their surface examined by scanning electron microscopy (SEM). Among the properties evaluated, the increase in the level of reinforcement caused a significant increase in the tensile strength and bending modulus of the composites compared to pure resin. The microstructural observations revealed the failure mechanisms that can occur during fracture, and that the area of natural coconut fiber contributes to good adhesion with DGEBA (diglycidyl ether of bisphenol A).
Keywords: Resina epóxi
Fibra de coco
Polímeros
Compósitos
Epoxy resin
Coconut fiber
Polymers
Composites
Subject CNPQ: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Language: por
Country: BR
Publisher / Institution : Universidade Federal de Sergipe
Institution: UFS
Program Affiliation: Pós-Graduação em Ciência e Engenharia de Materiais
Citation: GONÇALVES, Jorge Antônio Vieira. Compósitos à base de resina epóxi reforçados com fibra de coco. 2010. 60 f. Dissertação (Mestrado em Engenharia de Materiais) - Universidade Federal de Sergipe, São Cristóvão, 2010.
Rights: Acesso Aberto
URI: https://ri.ufs.br/handle/riufs/3485
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais

Files in This Item:
File Description SizeFormat 
JORGE_ANTONIO_VIEIRA_GONCALVES.pdf4,69 MBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.